Structural Adhesive Film

AF 30 (5, 10 and 12 mil)

MMM-A-132 Type I

Scotch-Weld AF 30

Class 2 & 3

(10 mil)

Requirement

with

Test Condition

Min. Ave.

Scotch-Weld EC-1660

A. Tensile Shear

psi

(MPa)

psi

(MPa)

1. Normal Temperature, 75°F (24°C)

2500

(17.2)

4218

(29.1)

2. 10 minutes @ 180°F (82°C)

1250

(8.6)

2440

(16.8)

3. 10 minutes @ -67°F (-55°C)

2500

(17.2)

4140

(28.5)

4. Normal Temperature 75°F (24°C) after 30 days immersion

2250

(15.5)

4000

(27.6)

in Salt Water Spray

5. Normal Temperature 75°F (24°C) after 30 days immersion

2250

(15.5)

4240

(29.2)

@ 120°F (49°C) and 95-100% Relative Humidity

6. Normal Temperature, 75°F (24°C) after 30 days immersion

2250

(15.5)

4050

(27.9)

in Tap Water

7. Normal Temperature, 75°F (24°C) after 7 days immersion

2250

(15.5)

3960

(27.3)

in JP-4 Fuel (MIL-T-5624)

8. Normal Temperature, 75°F (24°C) after 7 days immersion

2250

(15.5)

4130

(28.5)

in Anti-icing Fluid (MIL-F-5566)

9. Normal Temperature, 75°F (24°C) after 7 days immersion

2250

(15.5)

4070

(28.0)

in Hydraulic Oil (MIL-H-5606)

10. Normal Temperature, 75°F (24°C) after 7 days immersion

2250

(15.5)

3940

(27.1)

in Type III Hydrocarbon Fluid (MIL-S-3136)

MMM-A-132 Type I Class 2 Test Data – 3M™ Scotch-Weld™ Structural Adhesive Film AF 30 (10 mil)/

3M™ Scotch-Weld™ Structural Adhesive Primer EC-1660

The following is a summary and a list of average test results for the structural adhesive system Scotch-Weld AF 30

(10 mil) with primer when bonded specimens were prepared and tested in accordance with Military Specification

MMM-A-132, Type 1 Class 2.

B. Creep Rupture

11. Normal Temperature, 75°F (24°C) 192 hrs @ 1600 psi

0.015 inches (.381 mm)

0.003 inches (.076 mm)

(11.0 MPa)

max. deformation

12. 180°F (82°C), 192 hrs @ 800 psi (5.5 MPa)

0.015 inches (.381 mm)

0.006 inches (.152 mm)

max. deformation

C. Fatigue

13. Normal Temperature, 75°F (24°C) 750 psi (5.2 MPa) @

No glue line

No glue line

failure

failure

D. Other Tests

14. Normal Temperature, 75°F (24°C) T-Peel

Class 2: 15 piw

37 piw

(66.7 N/25 mm)

(164.6 N/25 mm)

Class 3:none

15. Tensile Shear, 75°F (24°C) Blister Detection

Class 2: 2250 psi

3885 psi

(15.5 MPa)

(26.8 MPa)

Class 3:none